Thermal responsive electrode structure for lithium-ion batteries

ABSTRACT

The present invention provides a thermally-decomposable consolidated polymer particle encapsulated-electrode for a lithium-ion battery. The electrode includes polymer particles including at least one connection unit and at least one crosslinker in an amount of approximately 40% to 98% by weight and at least one binder material in an amount of approximately from 2% to 60% by weight. The consolidated crosslinked polymer particle coating results in a porous structure encapsulating the electrode. The pressure resistance of the consolidated crosslinked polymer particle coating ranges approximately from 0.5 to 8 MPa and the consolidated crosslinked polymer particle coating is decomposed to release a non-flammable gas and phosphorous-containing molecules so as to prevent thermal runaway at a temperature approximately from 300° C. to 500° C.

CROSS-REFERENCE TO RELATED APPLICATIONS

The present application claims priority from the U.S. provisional patent application No. 63/116,929 filed Nov. 23, 2020, and the disclosure of which is incorporated by reference in its entirety.

FIELD OF THE INVENTION

The present invention relates to an electrode structure for a lithium-ion battery, in particular with polymer microspheres embedded in the nanofiber network for fire and thermal runaway prevention at a predetermined temperature.

BACKGROUND

With the rapid development of portable electronic devices and electric vehicles, lithium-ion batteries have dominated in the market for last decade. However, the development of current lithium-ion batteries is encountering safety issues such as: thermal runaway (TR) and TR-induced smoke, fire and explosion, which has been recognized as the major causes among the accidents of lithium-ion battery.

Abuse conditions are the main sources for TR including mechanical abuse (crush, penetration and drop, etc.), electrochemical abuse (short-circuit, overcharge and over-discharge, etc.), and thermal abuse (fire, thermal shock, and overheat, etc.). When the abuse is over the tolerance, it would initiate the thermal runaway to an unstoppable chain reaction. The temperature raises rapidly within milliseconds and the energy stored is suddenly released, which is able to induce a number of exothermic reactions including decomposition of the solid electrolyte interface (SEI) layer, oxidative/reductive decomposition of organic electrolytes at the anode/cathode surface, separator melt-down and the thermal decomposition of the material at the cathode. Meanwhile, a sharp increase in the internal pressure will also build up and more heat would add up, which in turn burns the electrolyte and ignites fire.

Therefore, there is a need in the art for a new type of design for the electrode structure of lithium batteries which is able to react immediately and to hinder the thermal runaway reaction in a short time period.

SUMMARY OF THE INVENTION

This section aims to summarize some aspects of the embodiments of the present invention and to briefly describe some preferred embodiments. The simplification or omission may be made in this section, the abstract of the specification, and the title to avoid obscuring the purpose of this section, the abstract of the specification, and the title. Such simplification or omission may not be used to limit the scope of the present invention.

Accordingly, a first aspect of the present invention provides a thermally-decomposable consolidated polymer particle encapsulated-electrode for a lithium-ion battery. The thermally-decomposable consolidated polymer particle encapsulated-electrode includes an electrode selected from a cathode, an anode, at least one binder material, and a consolidated crosslinked polymer particle coating forming a porous structure encapsulating the electrode. The polymer particles with the diameter approximately from 0.05 μm to 8 μm include at least one connection unit and at least one crosslinker having an amount of approximately from 25% to 50% by weight of the polymer particles. The connection unit and crosslinker have at least one cyclic compound analogue including one or more non-flammable gas unit and phosphorous-containing unit. The amount of binder material is approximately from 2% to 60% by weight and the amount of polymer particles is approximately from 40% to 98% by weight. In addition, the pressure resistance of the consolidated crosslinked polymer particle coating ranges approximately from 0.5 to 8 MPa and the consolidated crosslinked polymer particle coating decomposes to release a non-flammable gas and phosphorous-containing molecules so as to prevent fire and thermal runaway at a temperature approximately from 300° C. to 500° C.

In one embodiment of the present invention, the shape of the polymer particles includes regular-shaped spherical particles, irregular-shaped particles, rods, tubes and tubes.

In one embodiment of the present invention, the thickness of the consolidated crosslinked polymer particle coating is approximately from 3 μm to 40 μm.

In one embodiment of the present invention, the binder is selected from a group consisting of polyvinylidene fluoride (PVDF), poly(acrylic acid) (PAA), polyurethane (PU), poly(methyl methacrylate) (PMMA), poly(vinylidene fluoride-hexafluoroprolene) (PVDF-HFP), polyacrylonitrile (PAN), poly(vinyl alcohol) (PVA), cellulose.

In one embodiment of the present invention, the non-flammable gas unit and phosphorous-containing unit further includes elements selected from P, N, Cl, S, O, F, Br, C, Si and Al.

In one embodiment of the present invention, the connection unit is made of cyclotriphosphazene.

In one embodiment of the present invention, the crosslinker is selected from a group consisting of sulfonyldiphenol, bisphenol AF and melamine.

In one embodiment of the present invention, the consolidated crosslinked polymer particle coating is fabricated by methods selected from ultrasonic spraying, electrostatic spraying, doctor blade coating, slit coating, micro gravure coating and spin coating.

In one embodiment of the present invention, the porosity of the consolidated crosslinked polymer particle coating is approximately from 25% to 80%.

In one embodiment of the present invention, the non-flammable gas includes nitrogen, ammonia, carbon dioxide, sulfur dioxide and water vapor.

In one embodiment of the present invention, the phosphorous-containing molecules includes phosphorous based free radicals (e.g., PO., PO₂., HPO₂., etc.), phosphonic acid derivatives and polyphosphoric acid derivatives.

In one embodiment, it is provided a lithium-ion battery including the thermally-decomposable consolidated polymer particle encapsulated-electrode of the present invention.

BRIEF DESCRIPTION OF THE DRAWINGS

Embodiments of the present invention are described in more detail hereinafter with reference to the drawings.

FIG. 1 illustrates the consolidated crosslinked polymer particle and the binder forming a coated layer encapsulating the electrode of the present invention.

FIG. 2 shows the examples of connection units and crosslinkers.

FIG. 3 illustrates the chemical structure of fully cross-linked polymer PCPS

FIG. 4 illustrates the chemical structure of fully cross-linked polymer PCAF

FIG. 5A shows the morphology of PCPS particles with an average particle size of approximately 5 μm;

FIG. 5B shows the morphology of PCPS particles with an average particle size of approximately 3 μm;

FIG. 5C shows the morphology of PCPS particles with an average particle size of approximately 0.6 μm.

FIG. 6 shows the morphology of PCAF particles with the particle size approximately 2 μm.

FIG. 7A shows the result of liquid electrolyte wetting test for graphite anode without PCPS coated layer;

FIG. 7B shows the result of liquid electrolyte wetting test for graphite anode with PCPS coated layer (PCPS particle size: approximately 0.6 μm, coated layer thickness: 25 μm).

FIG. 8 illustrates the result of SEM-EDX for PCPS particles (particle size: approximately 0.6 μm).

FIG. 9 illustrates the result of SEM-EDX for PCAF particles (particle size: approximately 2 μm).

FIG. 10 shows the result of DSC for PCPS particles (particle size: approximately 0.6 μm)

FIG. 11 shows the result of TGA for PCPS particles (particle size: approximately 0.6 μm)

FIG. 12A shows the SEM photo for graphite anode without PCPS coated layer;

FIG. 12B shows the SEM photo for graphite anode with PCPS coated layer (PCPS particle size: approximately 0.6 μm, coated layer thickness: 25 μm);

FIG. 12C shows the SEM photo for graphite anode with PCPS coated layer (PCPS particle size: approximately 0.6 μm, coated layer thickness: 30 μm);

FIG. 13A shows the result of SEM for LiCoO₂ (LCO) cathode without PCPS coated layer;

FIG. 13B shows the result of SEM for LiCoO₂ (LCO) cathode with PCPS coated layer (PCPS particle size: approximately 0.6 μm, coated layer thickness: 20 μm);

FIG. 13C shows the result of SEM for LiCoO₂ (LCO) cathode with PCPS coated layer (PCPS particle size: approximately 0.6 μm, coated layer thickness: 30 μm).

FIG. 14 illustrates the result of C-rate performance for assembling graphite/Li half cell.

FIG. 15 illustrates the result of C-rate performance for assembling LiCoO₂ (LCO)/Li half cell.

FIG. 16 shows the result of nail penetration test (curve of Temperature-Time) for the assembly of LiCoO₂ (LCO)/graphite full cell. The thickness of the coated layer is approximately 20 μm on LCO cathode.

FIG. 17 shows the result of nail penetration test (curve of Temperature-Time) for the assembly of LiCoO₂ (LCO)/graphite full cell. The thickness of the coated layer is approximately 28 μm on graphite anode.

FIG. 18 shows the result of short circuit test (curve of Temperature-Time) for the assembly of LiCoO₂ (LCO)/graphite full cell. The thickness of the coated layer is approximately 14 μm on graphite anode.

FIG. 19 shows the result of short circuit test (curve of Temperature-Time) for the assembly of LiCoO₂ (LCO)/graphite full cell. The thickness of the coated layer is approximately 14 μm on LCD cathode.

DEFINITION

References in the specification to “one embodiment”, “an embodiment”, “an example embodiment”, etc., indicate that the embodiment described can include a particular feature, structure, or characteristic, but every embodiment may not necessarily include the particular feature, structure, or characteristic. Moreover, such phrases are not necessarily referring to the same embodiment. Further, when a particular feature, structure, or characteristic is described in connection with an embodiment, it is submitted that it is within the knowledge of one skilled in the art to affect such feature, structure, or characteristic in connection with other embodiments whether or not explicitly described.

The terms “a” or “an” are used to include one or more than one and the term “or” is used to refer to a nonexclusive “or” unless otherwise indicated. In addition, it is to be understood that the phraseology or terminology employed herein, and not otherwise defined, is for the purpose of description only and not of limitation. Furthermore, all publications, patents, and patent documents referred to in this document are incorporated by reference herein in their entirety, as though individually incorporated by reference. In the event of inconsistent usages between this document and those documents so incorporated by reference, the usage in the incorporated reference should be considered supplementary to that of this document; for irreconcilable inconsistencies, the usage in this document controls.

DETAILED DESCRIPTION

In the following description, many specific details are set forth for fully understanding of the present invention, but the present invention can also be implemented in other ways different from those described here, and those skilled in the art can make similar applications without departing from the scope of the present invention, Therefore the present invention should not be limited by the specific embodiments disclosed below.

The present invention provides an electrode encapsulated by a thermally-decomposable consolidated polymer particle for a lithium-ion battery. Advantageously, the consolidated crosslinked polymer particle coating forms a porous structure encapsulating the electrode and is able to decompose to release a non-flammable gas and phosphorous-containing molecules so as to prevent fire and thermal runaway at a temperature approximately from 300° C. to 500° C.

As shown in FIG. 1, the consolidated crosslinked polymer particle and binder form a coated layer on at least one side of the electrode. The thickness of the coated layer, i.e., the consolidated crosslinked polymer particle, is approximately from 3 μm to 40 μm, and the diameter of the polymer particle is approximately from 0.05 μm to 8 μm with the shape including regular-shaped spherical particles, irregular-shaped particles, rods, tubes and tubes. This coated layer not only provides non-flammable gas and phosphorous-containing molecules to prevent fire and thermal runaway at higher temperature but also has good pressure resistance ranging approximately from 0.5 to 8 MPa. Methods for fabricating this coated layer encapsulating the electrodes include, but not limited to ultrasonic spraying, electrostatic spraying, doctor blade coating, slit coating, micro gravure coating and spin coating.

In addition, the electrode of the present invention comprises a cathode or an anode, wherein the cathode includes a lithium-based material selected from the group consisting of lithium manganese oxide (LMO), lithium cobalt oxide (LCO), lithium nickel Manganese cobalt oxide (NMC), and lithium iron phosphate (LFP) and the anode is selected from the group consisting of graphene, graphite, lithium titanate (LTO), a silicon compound, a silicon carbon composite, a tin-containing compound, and a tin-based composite. Meanwhile, the coated layer, i.e. the consolidated crosslinked polymer particle, comprises polymer particles in an amount of approximately from 40% to 98% by weight and at least one binder material in an amount of approximately from 2% to 60% by weight. The polymer particles include at least one connection unit and at least one crosslinker, in which the connection unit and the crosslinker have at least one cyclic compound analogue structure with one or more non-flammable gas unit and phosphorous-containing unit. Referring to FIG. 2, FIG. 3 and FIG. 4, the connection unit is cyclotriphosphazene which would react with at least one crosslinker selected from the group consisting of sulfonyldiphenol, bisphenol AF and melamine to form a plurality of fully cross-linked polymer particles. As shown in FIGS. 5A to 5C, it illustrates the morphology of the fully cross-linked polymer particles, poly(cyclotriphosphazene-c-sulfonyldiphenol (PCPS), with an average particle size ranging approximately from 0.6 μm to 5 μm. Furthermore, as shown in FIG. 6, it illustrates the morphology of the fully cross-linked polymer particles, poly(cyclotriphosphazene-c-Bisphenol AF (PCAF). The coated layer fabricated by the fully cross-linked polymer particles, PCPS or PCAF, will result in a porous structure with a porosity approximately from 25% to 80%. Advantageously, the porous structure of the coated layer is able to maintain good mechanical strength and conductivity. In addition, the porous coating layer provides with a good wetting performance of liquid electrolyte and waterproof property (shown in FIG. 7A and FIG. 7B), which could avoid deterioration of liquid electrolyte and reduce production of by-products due to the introduction of moisture in the battery system.

In addition, due to the presence of the non-flammable gas unit and phosphorous-containing unit, the coated layer of the present invention improves the safety of the battery and is able to avoid thermal runaway at a temperature approximately from 300° C. to 500° C. The non-flammable gas unit and phosphorous-containing unit further include one or more elements, but not limited to, P, N, Cl, S, 0, F, Br, C, Si and Al. As shown in FIG. 8 and FIG. 9, those elements are abundant in PCPS and PCAF particles. Polymer particles with these two types of units such as PCPS and PCAF particles in the present invention exhibit efficient flame retardancy due to following reasons: (1) high phosphorus content in the polymer particles is able to decompose and release certain amounts of phosphorus molecules such as phosphorous based free radicals (e.g., PO., PO₂., HPO₂., etc.), phosphonic acid derivatives and polyphosphoric acid derivatives while overheating, which is able to eliminate and lower the flame of radicals such as H and OH so as to terminate the combustion reaction; (2) phosphorus compounds would form a non-flammable liquid film during decomposition so as to cover the electrode and isolate thereof from air, resulting in a flame-retardant effect; (3) some incombustible gases or non-flammable gases such as NH₃ and N₂, will be generated during the decomposition process so as to suppress the combustion by decreasing the concentration of the combustible gas(es).

Example

In order to realize the thermal effects of the polymer particles, PCPS particles with an average particle size of approximately 0.6 μm have been heated gradually from room temperature to about 350° C. to obtain a DSC curve as shown in FIG. 10. The DSC curve in FIG. 10 presented barely significant thermal effects during the measurement, suggesting that PCPS particles were quite stable at various temperatures within the afore-mentioned range. Furthermore, thermogravimetric (TGA) analysis has also been performed to measure the thermal stability and the fraction of decomposable components by monitoring the weight change of the polymer particles of the present invention during the heating. As shown in FIG. 11, PCPS particles were decomposed at approximately from 400° C. to 500° C., resulting in weight loss of 46.3%.

Referring to FIGS. 12A, 12B and 12C, the SEM photos of graphite anode without coating, graphite anode coated with a layer of two different thicknesses of PCPS particles having 0.6 μm particle size, respectively, are provided (FIG. 12B: coated layer thickness: 25 μm; FIG. 12C: coated layer thickness: 30 μm).

Referring to FIGS. 13A, 13B and 13C, the SEM photos of LiCoO₂ (LCO) cathode without coating, LCO anode coated with a layer of two different thicknesses of PCPS particles having 0.6 μm particle size, respectively, are provided (FIG. 13B: coated layer thickness: 20 μm; FIG. 13C: coated layer thickness: 30 μm).

The C-rate performance of a coin cell with or without the coated layer are also tested. As shown in FIG. 14, the C-rate performance of the assembly of graphite/Li half cell with the coated layer is similar to that without the coated layer, where the coin cell is 2032-type coin cell with 0.001V-2.0V; graphite mass loading: 11.7 mg cm⁻¹; separator thickness: 25 μm; electrolyte: 1 M LiPF6 EC-DEC-DMC=1:1:1 (by volume); PCPS particle size: approximately 0.6 μm; and the thickness of the coated layer is approximately 27 μm (only for the assembly with the coated layer). Meanwhile, as shown in FIG. 15, the C-rate performance of the assembly of LiCoO₂ (LCO)/Li half cell with the coated layer is also similar to that without the coated layer, where the coin cell is 2032-type coin cell with 3.0V-4.35V; LCO mass loading: 25.5 mg cm⁻¹; separator thickness: 25 μm; electrolyte: 1 M LiPF₆ EC-DEC-DMC=1:1:1 (by volume); PCPS particle size: approximately 0.6 μm; and the thickness of the coated layer is approximately 28 μm (only for the assembly with the coated layer). These results suggested that the coated layer will not impact on the C-rate performance of the lithium-ion battery.

Furthermore, as shown in Table 1, nail penetration test has been performed on the pouch cell without or with a layer of PCPS particles in various thicknesses on the LCO cathode thereof, i.e., 20, 24, and 28 μm, wherein the pouch cell is 461045-type pouch cell with a volumetric energy density higher than 450 WL⁻¹, voltage: 3.0V-4.35V, fully charged (100% SOC), LCO mass loading: 25.5 mgcm⁻¹, graphite mass loading: 11.7 mg cm⁻¹, separator thickness: 7 μm, electrolyte: 1 M LiPF₆ EC-DEC-DMC=1:1:1 (by volume), PCPS particle size: approximately 0.6 μm.

Referring to FIG. 16 and FIG. 17, having the thickness of the PCPS coated layer in 20 μm on LCO cathode or 28 μm on graphite anode, the Tmax were 75.5° C. at approximately 50 to 100 seconds and 111.5° C. at approximately 150 to 200 seconds after the nail penetration test. However, the batteries without the PCPS coated layer experience dramatically temperature rises after penetrations, with the Tmax soaring up to 661.4° C.

TABLE 1 The results of nail penetration test for assembly of LiCoO₂ (LCO)/graphite full cell Thickness of PCPS Sample coated layer (μm) Leakage Smoke Fire Results With PCPS 28 No NO NO 3/3 pass coated layer-1 With PCPS 20 No NO NO coated layer-2 With PCPS 24 No NO NO coated layer-3 Without PCPS — Yes Yes Yes 0/3 pass coated layer-1 Without PCPS — Yes Yes Yes coated layer-2 Without PCPS — Yes Yes Yes coated layer-3

As shown in Table 2, short circuit test has been further performed on the pouch cell without or with the coated layer on LCO cathode in various thicknesses, i.e. 14, 21, and 23 μm, wherein the pouch cell is 461045-type pouch cell with a volumetric energy density higher than 450 WL⁻¹, voltage: 3.0V-4.35V, fully charged (100% SOC), LCO mass loading: 25.5 mgcm⁻¹, graphite mass loading: 11.7 mg cm⁻¹, separator thickness: 7 μm, electrolyte: 1 M LiPF₆ EC-DEC-DMC=1:1:1 (by volume), PCPS particle size: approximately 0.6 μm.

Referring to FIG. 18 and FIG. 19, having the thickness of the PCPS coated layer in 14 μm on graphite anode and on LCO cathode, respectively, the Tmax were 127.3° C. at approximately 0 to 50 seconds and 129.9° C. at approximately 0 to 50 seconds after the short circuit test. However, the batteries without the PCPS coated layer experienced dramatic temperature rise after short circuit, with the Tmax up to 731.4° C. These results suggest that the internal short-cutting is efficiently inhibited due to the coated layer, thereby achieving a significant improvement in safety performance of the batteries.

TABLE 2 The results of short circuit test for assembly of LiCoO₂ (LCO)/graphite full cell Thickness of PCPS Sample coated layer (μm) Leakage Smoke Fire Results With PCPS 14 No NO NO 3/3 pass coated layer-1 With PCPS 21 No NO NO coated layer-2 With PCPS 23 No NO NO coated layer-3 Without PCPS — Yes Yes Yes 0/3 pass coated layer-1 Without PCPS — Yes Yes Yes coated layer-2 Without PCPS — Yes Yes Yes coated layer-3

It will be appreciated by those skilled in the art, in view of these teachings, that alternative embodiments may be implemented without deviating from the spirit or scope of the invention, as set forth in the appended claims. This invention is to be limited only by the following claims, which include all such embodiments and modifications when viewed in conjunction with the above specification and accompanying drawings. 

1. A thermally-decomposable consolidated polymer particle encapsulated-electrode for a lithium-ion battery comprising: an electrode selected from a cathode including a lithium-based material selected from the group consisting of lithium manganese oxide (LMO), lithium cobalt oxide (LCO), lithium nickel manganese cobalt oxide (NMC), and lithium iron phosphate (LFP), or an anode selected from the group consisting of graphene, graphite, lithium titanate (LTO), a silicon compound, a silicon carbon composite, a tin-containing compound, and a tin-based composite; a consolidated crosslinked polymer particle coating forming a porous structure encapsulating the electrode, the consolidated crosslinked polymer particle coating comprising: a plurality of polymer particles including at least one connection unit and at least one crosslinker, wherein the at least one connection unit and the at least one crosslinker have at least one cyclic compound analogue structure including one or more non-flammable gas units and phosphorous-containing units; at least one binder material in an amount of approximately 2% to 60% by weight; wherein the polymer particles are in an amount of approximately 40% to 98% by weight; wherein the at least one crosslinker is in an amount of approximately from 25% to 50% by weight of the polymer particles; wherein the diameter of the polymer particle is approximately from 0.05 μm to 8 μm; wherein the pressure resistance of the consolidated crosslinked polymer particle coating ranges approximately from 0.5 to 8 MPa; wherein the consolidated crosslinked polymer particle coating is decomposed to release a non-flammable gas and phosphorous-containing molecules so as to prevent fire and thermal runaway at a temperature approximately from 300° C. to 500° C.
 2. The thermally-decomposable consolidated polymer particle encapsulated-electrode for a lithium-ion battery of claim 1, wherein the shape of the polymer particles includes regular-shaped spherical particles, irregular-shaped particles, rods, tubes and tubes.
 3. The thermally-decomposable consolidated polymer particle encapsulated-electrode for a lithium-ion battery of claim 1, wherein the thickness of the consolidated crosslinked polymer particle coating is approximately from 3 μm to 40 μm.
 4. The thermally-decomposable consolidated polymer particle encapsulated-electrode for a lithium-ion battery of claim 1, wherein the binder is selected from the group consisting of polyvinylidene fluoride (PVDF), Poly(acrylic acid) (PAA), Polyurethane (PU), poly(methyl methacrylate) (PMMA), poly(vinylidene fluoride-hexafluoroprolene) (PVDF-HFP), polyacrylonitrile (PAN), poly(vinyl alcohol) (PVA), cellulose.
 5. The thermally-decomposable consolidated polymer particle encapsulated-electrode for a lithium-ion battery of claim 1, wherein the non-flammable gas unit and phosphorous-containing unit further includes elements selected from P, N, Cl, S, O, F, Br, C, Si and Al.
 6. The thermally-decomposable consolidated polymer particle encapsulated-electrode for a lithium-ion battery of claim 1, wherein the connection unit is cyclotriphosphazene.
 7. The thermally-decomposable consolidated polymer particle encapsulated-electrode for a lithium-ion battery of claim 1, wherein the crosslinker is selected from the group consisting of sulfonyldiphenol, bisphenol AF and melamine.
 8. The thermally-decomposable consolidated polymer particle encapsulated-electrode for a lithium-ion battery of claim 1, wherein the consolidated crosslinked polymer particle coating is fabricated by methods selected from ultrasonic spraying, electrostatic spraying, doctor blade coating, slit coating, micro gravure coating and spin coating.
 9. The thermally-decomposable consolidated polymer particle encapsulated-electrode for a lithium-ion battery of claim 1, wherein the consolidated crosslinked polymer particle coating has a porosity of approximately 25% to 80%.
 10. The thermally-decomposable consolidated polymer particle encapsulated-electrode for a lithium-ion battery of claim 1, wherein the non-flammable gas includes nitrogen, ammonia, carbon dioxide, sulfur dioxide and water vapor.
 11. The thermally-decomposable consolidated polymer particle encapsulated-electrode for a lithium-ion battery of claim 1, wherein the phosphorous-containing molecules include phosphorous based free radicals (e.g., PO., PO₂., HPO₂., etc.), phosphonic acid derivatives and polyphosphoric acid derivatives.
 12. A lithium-ion battery comprising the thermally-decomposable consolidated polymer particle encapsulated-electrode of claim
 1. 